RTP 203 MG GB 20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rh4BRu_RTP-203-MG-GB-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 230 MG GB 20 is reinforced with 20% milled glass and 20% glass bead. This material is a problem solver, it should be considered where warpage and moldability are critical. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8270 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 82.7 | MPa | ASTM D638 |
| -- | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 124 | MPa | ASTM D790 |
| Yield | 124 | MPa | ASTM D790 |
| Compressive Strength | 117 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 249 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 243 | °C | ASTM D648 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.48 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 12mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 274 - 288 | °C | |
| Middle Temperature | 274 - 288 | °C | |
| Front Temperature | 274 - 288 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 82.7 - 124 | MPa | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ARCEL® 730 (1.50 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| INTEGRAL™ 816 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |
| Karina IVORY PVC COMPOUND 937-35/1-B-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LONGLITE® PBT 3050-104X | CCP Group | PBT | LONGLITE® PBT |
| PONACOM PS 5570-10 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |