NORYL™ GTX870 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rgaqMF_NORYL-GTX870-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PA, Glass 20% |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 118 | MPa | Internal Method |
| Yield 1 | 122 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 12 | % | Internal Method |
| Break 2 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5680 | MPa | ASTM D790 |
| Flexural Strength | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 200 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 4.0E-5 to 6.0E-5 | cm/cm/°C | ASTM E831 |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zythane® 3045DX | Alliance Polymers & Services | TPU-Capro | Zythane® |
| FHR Polypropylene P6C6B-134 | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Karina BLACK PVC COMPOUND 700-48/ 1-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 65-8570/BL | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |
| RTP 1799 X 138211 C | RTP Company | PPE+PS | RTP |