SABIC® LDPE PCG22
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rgVGPX_SABIC-LDPE-PCG22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG22 is an additive free grade, typically designed for healthcare packaging and can typically be converted by Injection Molding to produce caps and closures. It exhibits a high MFR for good flow properties. Compliance to Regulations SABIC® LDPE PCG22 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 22 | g/10 min | |
| 190°C/5.0 kg | 75 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 29.0 | cm³/10min | |
| 190°C/5.0 kg | 98.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 175 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 8.00 | MPa | |
| Break, 2.00 mm, Compression Molded | 7.00 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 400 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 80.0 | MPa | |
| 1000 hr | 45.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 5.0 | kJ/m² | |
| 23°C, Compression Molded | 42 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 39.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 82.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 105 | °C | DIN 53765 |
| Enthalpy Change | 104 | J/g | DIN 53765 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN5002SF | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Borealis PP BA160E-8229-01 | Borealis AG | PP Impact Copolymer | Borealis PP |
| Celstran® PP-GF50-02-Black | Celanese Corporation | PP, Unspecified | Celstran® |
| Fiberfil® M-2450 | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| Glastic® UTS 141 | Glastic Corporation | Polyester, TS | Glastic® |