VYPET VNT 615HP
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lavergne Group |
| Trademark: | VYPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rgTGlZ_VYPET-VNT-615HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vypet VNT 615 HP is a modified 15% fiberglass reinforced PET injection molding compound designed for automotive structural applications. Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 0.40 | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.80 | % | ASTM D955 |
| Ash Content | 15 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 6000 | MPa | ISO 178 |
| Flexural Stress 2 | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | °C | ISO 75-2/A |
| Melting Temperature | 250 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 275 - 295 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 95.0 - 120 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Injection Pressure: MediumBack Pressure: LowScrew Speed: Medium |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ CRS5211R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Xuchuan XCW-6021(A) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Arnitel® PM381 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| Hiprolon® 11 ESNWHL | Arkema | Nylon 1012 | Hiprolon® |
| LNP™ THERMOCOMP™ XF006S compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOCOMP™ |