Ultradur® B 4300 M5
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rgPZoR_Ultradur-B-4300-M5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25 % mineral reinforced injection molding grade for parts with good surface finish and low warpage tendency (eg housings and visible partson home appliances). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.7 | % | |
| Flow | 1.8 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number 1 | 117 | cm³/g | ISO 307 |
| Mold Shrinkage 2 | |||
| free, longitudinal | 1.7 | % | |
| free, transverse | 1.8 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 200 | °C | |
| Temperature Index - at 50% loss of tensile strength | IEC 60216 | ||
| -- 3 | 120 | °C | |
| -- 4 | 130 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 250 | mm/sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 56.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 7.5 | % | ISO 527-2 |
| Tensile Creep Modulus 5(1000 hr) | 2000 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 195 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 7.0E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1500 | J/kg/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.2E-3 | ||
| 1 MHz | 0.015 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 225 | V | |
| Solution B | 150 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.400 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Processing (Melt) Temp | 250 to 275 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 2 . | plate with film gate 150*150*3 mm³ |
| 3 . | 20000 h |
| 4 . | 5000 h |
| 5 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M80063 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| DOWLEX™ 2006G | The Dow Chemical Company | HDPE | DOWLEX™ |
| Innova R 970E | Innova SA | PS (HIPS) | Innova |
| OTECH TPO OTR8588 - Cord Jacket | OTECH Corporation | TPO | OTECH TPO |
| LNP™ STAT-KON™ DD000 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |