Hostacom 6652
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rfIV8K_Hostacom-6652.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom 6652 low melt flow, 1,650 MPa flexural modulus polypropylene homopolymer has high strength, excellent impact resistance and good hydrolytic stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.940 | g/cm³ | ASTM D792 |
| 23°C | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 2.0 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 1.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 to 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 34.0 | MPa | ASTM D638, ISO 527-2 |
| Break | 19.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield | 9.0 | % | ASTM D638, ISO 527-2 |
| Break | 250 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 1400 | MPa | ASTM D790 |
| -- | 1650 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256A |
| -- | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 88.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 104 | °C | ISO 75-2/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D TFE 15 | RTP Company | Nylon 612 | RTP |
| SLOVAMID® 6 GF 65 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| LNP™ THERMOCOMP™ RX10405H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| O'Tech OW 645 | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Integra™ PP 2200 LE | PolySource, LLC | PP Impact Copolymer | Integra™ |