Reny® 1002H
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rdzNzT_Reny-1002H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® 1002H is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1002H: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 41 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 31.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.51 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.20 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12100 | 11100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 181 | 148 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.7 | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 11600 | 10700 | MPa | ISO 178 |
| Flexural Stress | 286 | 265 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.3 | 6.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | 33 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 237 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 224 | 212 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 7.0E+14 | 2.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 2.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 1.00 mm | 31 | 29 | kV/mm | |
| 2.00 mm | 27 | 22 | kV/mm | |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | -- | 5.00 | ||
| 1 MHz | -- | 4.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | -- | 0.020 | ||
| 1 MHz | -- | 0.016 | ||
| Comparative Tracking Index | 525 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoFlo 30A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| Nanjing Hongrui PA66 A309 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Edgetek™ AT-15GB/000 BLACK | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| Grilamid® LV-50H FWA black 9225 | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Hifax CA 217 A | LyondellBasell Industries | PP Copolymer | Hifax |