Starflam P10003
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rdwMue_Starflam-P10003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflam P10003 is a Mineral Flame Retardant, Halogen Free, Red Phosphorous Free, Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 1.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 71.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6200 | MPa | ISO 178 |
| Flexural Stress | 122 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 4.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 179 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 94.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.4E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.7E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm, Tested by E2P) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 245 to 255 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 55.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP KSR4525 | Borealis AG | PP, Unspecified | Borealis PP |
| Clariant Nylon 6/6 6618G15 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Comco PA 6 oil | Comco-Plastic GmbH | Nylon 6 | Comco |
| Delta GPT-20 | Delta Polymers | PP Homopolymer | Delta |
| Sylvin 2990-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |