RTV-2 P-60
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rbSCGh_RTV-2-P-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| P-60 is a high durometer, high modulus, platinum-catalyzed, RTV-2 silicone rubber designed for casting polyurethanes and epoxies. It is easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component siliconerubbers may show inhibition sensitivity. P-60 offers outstanding chemical and heat resistance and the rigidity to withstand the expansion of most polyurethane foams. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 343 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.809 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 14 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 95000 to 120000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Blue | ||
| -- 3 | Tan | ||
| Viscosity | |||
| -- 4 | 1.0 to 2.0 | Pa·s | |
| -- 5 | 130 to 160 | Pa·s | |
| Curing Time | 16 to 24 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 6 | 54 to 62 | ||
| Shore A 7 | 58 to 66 | ||
| Tensile Strength | 5.58 to 6.83 | MPa | ASTM D412 |
| Tensile Elongation at Break | 180 to 230 | % | ASTM D412 |
| Tear Strength | 11.4 to 14.9 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Activator |
| 3 . | Base |
| 4 . | Activator |
| 5 . | Base |
| 6 . | 1 Day |
| 7 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® LFT PA A1350 | SAMBARK | Nylon 66 | SUPRAN® LFT PA |
| ADENE OTJB | A.D. Compound spa | PP Homopolymer | ADENE |
| Aurora PVC AP1271 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Hostacom EKG 286T Black | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Plexar® PX3227 | LyondellBasell Industries | LLDPE | Plexar® |