Durethan® BKV 35 XTS1 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rb45W9_DurethanBKV35XTS1901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 35 % glass fibers, injection molding, heat-aging stabilized, notably high heat-aging stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.73 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.91 | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.23 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.30 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 180 | MPa | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 10400 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 270 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.4 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-110, GF35 | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 70 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Melting Temperature 8 | 221 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC1003R resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| Stat-Tech™ NN-20CF/000 SO1 | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| VITAMIDE® BF13N2441/2 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Unichem 6812A-02 | Colorite Polymers | PVC, Flexible | Unichem |
| LNP™ THERMOCOMP™ RF003AXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |