LNP™ LUBRICOMP™ RAL22 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rZFwCp_LNPLUBRICOMPRAL22compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RAL22 is a compound based on PA66 resin containing PTFE, Aramid Fiber. Added Features: Internally Lubricated Also known as: LNP* LUBRICOMP* Compound RAL-4022 Product reorder name: RAL22 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.90 - 1.3 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 72.0 | MPa | ISO 527-2/5 |
| Fracture | 71.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 7.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3400 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 106 | MPa | ISO 178 |
| -- 4 | 109 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.54 | ASTM D3702 Modified | |
| With Self-Static | 0.45 | ASTM D3702 Modified | |
| Flexural Strain at Break 5 | 8.4 | % | ISO 178 |
| Wear Factor - Washer | 13.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(1.8 MPa, Unannealed, 64.0 mm Span) | 93.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break |
| 4 . | Yield |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 3662 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| UmaPET TFMH | Ester Industries Ltd. | PET | UmaPET |
| Karina IVORY PVC COMPOUND 750-35/1-B-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1105-7536 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Axiall PVC 8601 | Axiall Corporation | PVC, Flexible | Axiall PVC |