| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rZ5VAR_CYCOLACMG47Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. FDA compliant. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 5.6 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2270 | MPa | ASTM D638 |
| -- | 2370 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 44.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 33.0 | MPa | ASTM D638 |
| Fracture | 35.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2/50 |
| Fracture 5 | 24 | % | ASTM D638 |
| Fracture | 25 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 70.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 26 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 320 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 22 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 94.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 81.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ASTM D1525 13 |
| -- | 98.0 | °C | ISO 306/B50 |
| -- | 100 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 14 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 1000 sec^-1) | 225 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Rear Temperature | 188 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 216 - 238 | °C | |
| Nozzle Temperature | 218 - 260 | °C | |
| Processing (Melt) Temp | 218 - 260 | °C | |
| Mold Temperature | 48.9 - 71.1 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| 14 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VDC 250-40 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PVDC | TEKNIFLEX® |
| MORETEC™ 0218CM | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| Witcobond® W-505 | Chemtura | PUR-Ester | Witcobond® |
| PHOENIX™ 13551 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| Sylvin 8225-65 Orange 579 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |