Nylene® 724

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rYqfFH_Nylene-724.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Heat stabilized version of 721 which is a medium-impact modified nylon for fast, easy molding

In addition to heat stabilization to prevent thermal degradation, parts molded from Nylene 724 have good impact strength right out of the mold without post conditioning

Stiffness is near that of unmodified nylon 6

Barrel temperatures should be in the 450°F - 500°F range.

General Information
Additive	Heat Stabilizer Impact Modifier
Features	Good Moldability Heat Stabilized Impact Modified Medium Impact Resistance
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.10	g/cm³	ASTM D792
Molding Shrinkage - Flow	1.4	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	62.1	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	200	%	ASTM D638
Flexural Modulus (23°C)	2170	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-40°C	27	J/m
23°C	160	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	170	°C
1.8 MPa, Unannealed	62.8	°C
Peak Melting Temperature	221	°C	ASTM D3418

Injection	Nominal Value	Unit
Rear Temperature	232 to 260	°C
Middle Temperature	232 to 260	°C
Front Temperature	232 to 260	°C

Resin Grade	Manufacturer	Category	Trademark
TECASINT™ 2021	Ensinger Inc.	PI, TP	TECASINT™
TPUCO® TPUE-UEH80	Taiwan PU Corporation	TPU-Polyether	TPUCO®
TRIREX® 3030IR	Samyang Corporation	PC	TRIREX®
DINALON® B1S25 HI	Grupo Repol	Nylon 6	DINALON®
Hostacom TRC 411N R C13034	LyondellBasell Industries	PP, Unspecified	Hostacom