TECACOMP® PA66 GF30 TF15 HI black 3366
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rY7gBz_TECACOMPPA66GF30TF15HIblack3366.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | |
| Apparent Density | 0.69 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 50 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 38.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.98 | % | ISO 294-4 |
| Flow | 0.31 | % | ISO 294-4 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 143 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/50 |
| Tensile Stress | 160 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | °C | ISO 75-2/A |
| Glass Transition Temperature | DIN 53765 | ||
| -- 1 | 5.00 | °C | DIN 53765 |
| -- 2 | 72.0 | °C | DIN 53765 |
| Melting Temperature | 260 | °C | DIN 53765 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 260 - 310 | °C | |
| Mold Temperature | 90 - 150 | °C |
| Note Message | |
|---|---|
| 1 . | Moist |
| 2 . | Dry |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Regis® 6503 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| QR Resin QR-1805IMLM | QTR, Inc. | PC+Polyester | QR Resin |
| ELEVATE™ EF528 | Westlake Chemical Corporation | EVA | ELEVATE™ |
| Escorene™ Ultra UL 00728FF | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| PHOENIX™ 14701 | Phon Tech Industrial Company | TPE | PHOENIX™ |