LEXAN™ XHT4143T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rXfSFD_LEXAN-XHT4143T-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 24.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.95 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.33 | % | |
| Equilibrium, 23°C, 50% RH | 0.25 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2730 | MPa | ASTM D638 |
| -- | 2750 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 77.0 | MPa | ASTM D638 |
| Yield | 78.0 | MPa | ISO 527-2/50 |
| Break 3 | 69.0 | MPa | ASTM D638 |
| Break | 67.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Break 5 | 50 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2600 | MPa | ASTM D790 |
| -- 7 | 2600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 76 | J/m | ASTM D256 |
| 23°C | 93 | J/m | ASTM D256 |
| -30°C 11 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 72.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 174 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 14 | 173 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 165 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 15 | 162 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 183 | °C | ASTM D1525, ISO 306/B50 10 16 |
| -- | 181 | °C | ISO 306/B120 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 2.00 mm | 850 | °C | |
| 2.50 mm | 960 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.605 | ASTM D542 | |
| Transmittance (2540 µm) | 86.0 | % | ASTM D1003 |
| Haze (2540 µm) | 0.50 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 300 to 315 | °C | |
| Nozzle Temperature | 295 to 310 | °C | |
| Processing (Melt) Temp | 300 to 315 | °C | |
| Mold Temperature | 95.0 to 130 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 40 to 90 | rpm | |
| Vent Depth | 0.025 to 0.080 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | 80*10*4 mm |
| 16 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNIBRITE® UB-860 | Nippon A&L Inc. | AES | UNIBRITE® |
| Axiall PVC 39041 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hyundai EP PA66 LD610 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Jampilen EP332L | Jam Polypropylene Company | PP Copolymer | Jampilen |
| Hostacom EKC 330N E1 G72758 | LyondellBasell Industries | PP Copolymer | Hostacom |