Petlon R-Prime F3-T20-00-BK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petlon Polymers Ltd |
| Trademark: | Petlon R-Prime |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rXXss2_Petlon-R-Prime-F3-T20-00-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 100% Recycled Polypropylene, 20% Talc Filled, Black, Compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 10 to 22 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 160 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Corton® PDR 1623 HS | PolyPacific Pty. Ltd. | PP Homopolymer | Corton® |
| HiFill® POM CO 0167 S1 LE | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Jackdaw Nylon XI10NT6643 | Jackdaw Polymers | Nylon+PP | Jackdaw Nylon |
| LIHAN® C9704 | Nanjing Lihan Chemical Co., Ltd. | PC | LIHAN® |
| OTECH TPO OTO9588 - Cord Jacket | OTECH Corporation | TPO | OTECH TPO |