PLUSTEK PD1002NT
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rX97lR_PLUSTEK-PD1002NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity Polyamide 12 extrusion type. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.80 to 0.90 | % | ASTM D955 |
| -- | 0.80 to 0.90 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 1.2 | % | ASTM D570 |
| Saturation, 23°C | 1.2 | % | ISO 62 |
| Equilibrium | 0.70 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 70 | % | ASTM D638, ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact (23°C) | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 130 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ASTM D648, ISO 75-2/A |
| Maximum Use Temperature 1 | 150 | °C | |
| Maximum Continuous Use Temperature | 105 | °C | |
| Melting Temperature | 175 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | kV/mm | IEC 60250 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Short Peaks Operation |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9760 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TIPPLEN® K 691 | MOL Petrochemicals Co. Ltd. | PP Impact Copolymer | TIPPLEN® |
| TOTAL Polypropylene PPH 3827WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ABS Proquigel FR | Proquigel | ABS | ABS Proquigel |
| Capilene® T 89 E | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |