PRL PC/ABS-G10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rT6741_PRL-PC-ABS-G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRL PC/ABS-G10 is a Polycarbonate + ABS (PC+ABS) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 3.0 to 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 64.8 | MPa | |
| Break, 3.18 mm | 60.0 | MPa | |
| Flexural Modulus (3.18 mm) | 4000 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 124 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 116 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 to 288 | °C | |
| Middle Temperature | 254 to 293 | °C | |
| Front Temperature | 260 to 302 | °C | |
| Processing (Melt) Temp | 271 to 299 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 GK 30 black (2306) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Daelim Po1y® PP-247 | DAELIM INDUSTRIAL CO., LTD. | PP Impact Copolymer | Daelim Po1y® |
| Elasthane™ 75D | DSM Biomedical Inc. | TPU-Polyether | Elasthane™ |
| Huafon HF-1185A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| PLEXIGLAS® Sheet Resist 75 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |