Polidan® PNT 0555/06 Datasheet,XLPE,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
POLIDAN® PNT 0555/06 is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction. It is used for flexible crosslinkable pipes. Applications POLIDAN® PNT 0555/06 is used for the production of pipes for domestic hot and cold water supply as well as underfloor hating This compound is designed for both mono layer and composite pipe solutions.

General Information
Features	Crosslinkable Good flexibility
Uses	Pipe components Piping system
Processing Method	Pipeline extrusion molding Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.940	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.6	g/10 min	ISO 1133
Gel content- Crosslinking level	> 65	%	EN 579

Extrusion	Nominal Value	Unit
Head Temperature	200	°C
Extruder Screw L/D Ratio	25:1 ~ 30:1
Extruder Screw Compression Ratio	>2.5:1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	570	MPa	ISO 527-2
Tensile Strength	> 20.0	MPa	ASTM D638
Tensile Elongation (Break)	> 350	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	126	°C	ASTM D1525
Specific Heat (23°C)	2030	J/kg/°C	ISO 11357
Thermal Conductivity ¹(23°C)	0.45 - 0.47	W/m/K	Internal method

Additional Information
Above values are typical averages obtained from 18 x 2 mm mono layer pipe specimens which are extruded with 95 parts of POLIDAN® PNT 0555/06 and 5 parts of CATALYST PS/4. These pipe specimens are cured by immersion in hot water at 95°C for 6 hours time.Storage and Handling In order to avoid pre-mature crosslinking, the silane crosslinkable compound and the catalyst masterbatch shall be stored separately and mixed only when used. The silane crosslinkable compound shall be used within 6 - 8 hours after bags are opened. The product shall be stored under the following conditions: Closed and unbroken bags Ambient temperature not exceeding 40°C Indoor in order to avoid direct exposure to sunlight The product could undergo alterations due to extended period of storage. Solvay Specialty Polymers suggests the product use within six months from the production date printed on the packaging. Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled. Packaging POLIDAN® PNT 0555/06 is supplied in 500 kg octabins which contain a single moisture resistant bag or in 25 kg moisture resistant bags placed on 1375 kg pallets. Technical Service POLIDAN® PNT 0555/06 is part of the Solvay Specialty Polymers POLIDAN® PEX System product range. Solvay Specialty Polymers Technical Service is available to assist customers with further information and advice including the start-up and also for any eventual necessity during the use of the product.

Additional Information

Above values are typical averages obtained from 18 x 2 mm mono layer pipe specimens which are extruded with 95 parts of POLIDAN® PNT 0555/06 and 5 parts of CATALYST PS/4. These pipe specimens are cured by immersion in hot water at 95°C for 6 hours time.Storage and Handling In order to avoid pre-mature crosslinking, the silane crosslinkable compound and the catalyst masterbatch shall be stored separately and mixed only when used. The silane crosslinkable compound shall be used within 6 - 8 hours after bags are opened. The product shall be stored under the following conditions: Closed and unbroken bags Ambient temperature not exceeding 40°C Indoor in order to avoid direct exposure to sunlight The product could undergo alterations due to extended period of storage. Solvay Specialty Polymers suggests the product use within six months from the production date printed on the packaging. Solvay Specialty Polymers accepts no liability of any kind in case the above mentioned conditions are not fulfilled. Packaging POLIDAN® PNT 0555/06 is supplied in 500 kg octabins which contain a single moisture resistant bag or in 25 kg moisture resistant bags placed on 1375 kg pallets. Technical Service POLIDAN® PNT 0555/06 is part of the Solvay Specialty Polymers POLIDAN® PEX System product range. Solvay Specialty Polymers Technical Service is available to assist customers with further information and advice including the start-up and also for any eventual necessity during the use of the product.

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	150 - 200	°C
Cylinder Zone 2 Temp.	150 - 200	°C
Cylinder Zone 3 Temp.	150 - 200	°C
Cylinder Zone 4 Temp.	150 - 200	°C
Cylinder Zone 5 Temp.	150 - 200	°C
Die Temperature	210	°C

Extrusion instructions
Processing Guidelines The silane crosslinkable compound POLIDAN® PNT 0555/06 shall be used together with a Solvay Specialty Polymers catalyst masterbatch in the ratio of 95 to 5 parts respectively. Mixing shall be done just before extrusion or during the extrusion process with the use of automatic feeders. POLIDAN® PNT 0555/06 can be processed with modern PE single screw extruders. Curing The final pipe properties are curing dependent. Curing can be done in the following ways: by immersion in hot water at 90-95°C by circulation of hot water inside the pipe at 90-95°C by exposure to steam In all cases curing time depends on the pipe wall thickness, pipe structure and applied curing temperature. Colouring POLIDAN® compounds and catalyst masterbatches can be used together with good quality PE based colour masterbatches. Solvay Specialty Polymers suggests pre-drying all colour masterbatches prior to use.

Extrusion instructions

Processing Guidelines The silane crosslinkable compound POLIDAN® PNT 0555/06 shall be used together with a Solvay Specialty Polymers catalyst masterbatch in the ratio of 95 to 5 parts respectively. Mixing shall be done just before extrusion or during the extrusion process with the use of automatic feeders. POLIDAN® PNT 0555/06 can be processed with modern PE single screw extruders. Curing The final pipe properties are curing dependent. Curing can be done in the following ways: by immersion in hot water at 90-95°C by circulation of hot water inside the pipe at 90-95°C by exposure to steam In all cases curing time depends on the pipe wall thickness, pipe structure and applied curing temperature. Colouring POLIDAN® compounds and catalyst masterbatches can be used together with good quality PE based colour masterbatches. Solvay Specialty Polymers suggests pre-drying all colour masterbatches prior to use.

Note Message
1 .	Hot Plate Method

Category:	XLPE , Crosslinked Polyethylene
Manufacturer:	Solvay Specialty Polymers
Trademark:	Polidan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rSlqhG_Polidan-PNT-0555-06.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Xuchuan XCW-8230HT	Xuchuan Chemical (Suzhou) Co., Ltd	PUR, Unspecified	Xuchuan
CONTINUUM鈩?DMDD-6620 HEALTH+鈩?Datasheet	The Dow Chemical Company	HDPE	CONTINUUM™
EZPrene 9555A SHF	ENPLAST Americas, a Ravago Group Company	TPV	EZPrene
Flontech® FT-1-1L	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
LUVOCOM® 1105-0918/BL	Lehmann & Voss & Co.	PEEK	LUVOCOM®