Eltex® P CAP912

Category:	PP Random Copolymer , Polypropylene Random Copolymer
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex® P
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rSa5ok_Eltex-P-CAP912.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Benefits & Features
Eltex® P CAP912 is a random copolymer polypropylene specially developed for caps and closures applications in direct contact with beverages. Eltex® P CAP912 has excellent organoleptic properties – taste & odour – which are guaranteed and is compliant with volatile organic compound requirements following EPA524.2; this provides ultra-clean packaging capability.
Eltex® P CAP912 is a medium ethylene content random copolymer with good balance of stiffness, impact and processing. It offers for the injection moulding of caps and closures high transparency, surface aspect quality and hinge resistance.

Good transparency

Good flow

Good mould release

Good hinge properties

Excellent and quality controlled organoleptic properties. In order to preserve the excellent organoleptic properties, it is important not to exceed a melt temperature of 250°C during processing.

Applications
Caps and closures for the packaging of still beverages: water, juices, functionalised beverages,...

General Information
Features	Clean/High Purity Excellent Organoleptic Properties Good Flow Good Mold Release Good Surface Finish High Clarity Random Copolymer
Uses	Caps Closures
RoHS Compliance	Contact Manufacturer
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	13	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield, 23°C, Injection Molded)	28.0	MPa	ISO 527-2
Flexural Modulus (23°C, Injection Molded)	1100	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength			ISO 180/A
0°C, Injection Molded	3.3	kJ/m²
23°C, Injection Molded	6.0	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	90.0	°C	ISO 75-2/B
Vicat Softening Temperature	130	°C	ISO 306/A50
Peak Crystallization Temperature (DSC)	119	°C	Internal Method

Optical	Nominal Value	Unit	Test Method
Haze			ASTM D1003
1000 µm	15	%
2000 µm	30	%

Resin Grade	Manufacturer	Category	Trademark
DINALEN® 55	DIOKI d.d.	LDPE	DINALEN®
Karina IVORY PVC COMPOUND 750-35/1-B-AC-AS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Petrotene® PP A3 T40 HS UV PRTA010 PH382 MSP	Petropol Industry and Trade of Polymers LTDA	PP Homopolymer	Petrotene® PP
Hostacom TRC 103P G71322	LyondellBasell Industries	PP Copolymer	Hostacom
SQUARE® SSR3918-40	Shenzhen SQUARE Silicone Co., Ltd.	Silicone	SQUARE®