Toyolac® 700-314
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rRxsKD_Toyolac-700-314-79402.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 700-314 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 50.0 | MPa | ASTM D638 |
| 23°C | 54.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 35 | % | ASTM D638 |
| Break, 23°C | 18 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2450 | MPa | ASTM D790 |
| 23°C | 2540 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 76.0 | MPa | ASTM D790 |
| 23°C | 81.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 120 | J/m | |
| -30°C, 12.7 mm | 78 | J/m | |
| 0°C, 3.20 mm | 160 | J/m | |
| 0°C, 12.7 mm | 110 | J/m | |
| 23°C, 3.20 mm | 200 | J/m | |
| 23°C, 12.7 mm | 190 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 82.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5000A | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Teslin® SP 1400 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| 3M™ Dyneon™ Fluoroplastic FEP 6301Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| LTP PA6150 | Chengdu Letian Plastics Co., Ltd | TP, Unspecified | LTP |
| Lushan L-5R(HC) | Guangzhou Lushan New Materials Co., Ltd | PE Copolymer | Lushan |