Generic TS, Unspecified - Glass Fiber
| Category: | TS, Unspecified , Thermoset, Unspecified |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rQoNch_Generic-TS-Unspecified---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TS, Unspecified - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.74 - 1.90 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.041 - 0.25 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 - 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 44 - 45 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8750 - 15500 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 29.0 - 82.7 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 6660 - 12800 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 65.7 - 212 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 94.8 - 190 | MPa | ASTM D695 |
| Poisson's Ratio (23°C) | 0.30 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 13 - 1100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 320 - 1500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 - 205 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 2.5E-5 - 2.6E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 3.4E-5 - 3.5E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity (23°C) | 0.28 - 0.31 | W/m/K | ASTM C177 |
| RTI Elec | 129 - 130 | °C | UL 746 |
| RTI Imp | 130 - 131 | °C | UL 746 |
| RTI | 130 - 131 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C) | 12 - 18 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.54 - 5.26 | ASTM D150 | |
| Dissipation Factor (23°C) | 1.4E-3 - 0.018 | ASTM D150 | |
| Arc Resistance | 178 - 181 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 7.9 - 17 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 149 - 150 | °C | |
| Injection Pressure | 5.00 - 5.19 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TS, Unspecified - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV 15 Natural | Radici Plastics | Nylon 66 | Radilon® |
| SEPTON™ 4044 | Kuraray Co., Ltd. | SEEPS | SEPTON™ |
| Zytel庐 HTN FR52G30BL BK337 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Bayblend® FR3021 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Huafon HF-3785A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |