POLYTROPE® STR 1042EU-01 NATURAL
| Category: | Polyolefin, Enhanced TPO , Enhanced TPO Polyolefin |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYTROPE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rQPC1c_POLYTROPESTR1042EU01NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYTROPE STR 1042EU resin is a high melt strength thermoformable TPO that balances impact resistance and high stiffness, enabling processors and end users to reduce product weight and improve processing efficiency without sacrificing product performance. The attractive performance features of POLYTROPE STR 1042EU resin uniquely positions it as a economically favorable option to traditional engineered resins. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 1042EU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C, 24 hr, 3.18 mm) | 0.70 - 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 22.9 | MPa | ASTM D638 |
| Yield, 23°C 2 | 23.6 | MPa | ISO 527-2 |
| Tensile Strain 3(Break, 233°C) | > 200 | % | ISO 527-2 |
| Flexural Modulus - Chord 4(23°C) | 2510 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.1 | kJ/m² | ISO 179 |
| 23°C | 62 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| -30°C | 53 | J/m | ASTM D256 |
| 23°C | 860 | J/m | ASTM D256 |
| -30°C | 4.7 | kJ/m² | ISO 180 |
| 23°C | 54 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (-30°C, Total Energy, Ductile Failure) | 48.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 114 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 60.2 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -30 to 100°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.2 mm, All Colors) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, 3180 µm, Thermoformed, Smooth) | 20 - 40 | ISO 2813 |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1A, 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ DC-818.G001-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Toyolac® 920 555 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Nipol® LX407F | Zeon Corporation | Latex | Nipol® |
| Novodur® 640 | Styrolution | ABS | Novodur® |
| MAJ'ECO EFR060BS 9445 WHITE 3 | AD majoris | Biodeg Polymers | MAJ'ECO |