TECACOMP® PBT TC white 4038
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rPzQHy_TECACOMPPBTTCwhite4038.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.98 | g/cm³ | |
| Apparent Density | 1.00 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 120 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 135 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.7 | % | ISO 294-4 |
| Flow | 1.6 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2/50 |
| Tensile Stress | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 6200 | MPa | ISO 178 |
| Flexural Stress 2 | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 17 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 155 | °C | ISO 75-2/A |
| Glass Transition Temperature | 60.0 | °C | DIN 53765 |
| Melting Temperature | 225 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 40°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 60 to 110°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 40°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 60 to 110°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 3 | 1.3 | W/m/K | DIN EN 821 |
| -- 4 | 1.4 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.3E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 4.0E+13 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 130 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Through-plane |
| 4 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Europrene® SOL TH 2314 | Versalis S.p.A. | SEBS | Europrene® |
| Hylon® N1015THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Jiangsu Meilan XXMLF2-15 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |
| LNP™ LUBRICOMP™ FX04491H compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |
| LUVOCOM® 50-7078/GY-HB | Lehmann & Voss & Co. | PC | LUVOCOM® |