FRIANYL® B3 V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | FRIANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rOiaIz_FRIANYLB3V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
FLAME RETARDANT COMPOUND
PA6, UNFILLED, FLAME RETARDANT V0 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 23°C | 1.5 | % | ISO 294-4 |
| Flow : 23°C | 1.5 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 2.0 | % | ISO 62 |
| Saturated, 23°C | 8.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3450 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 8.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 185 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 125 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 165°C | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Needle Flame Test | IEC 60695-11-5 | ||
| 1.00 mm | Pass | IEC 60695-11-5 | |
| 2.00 mm | Pass | IEC 60695-11-5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.40 mm | V-0 | UL 94 | |
| 0.8 mm | V-0 | UL 94 | |
| 1.6 mm | V-0 | UL 94 | |
| 3.2 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.8 mm | 960 | °C | IEC 60695-2-12 |
| 3.2 mm | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PVC VSL-4610-N | Sumitomo Bakelite Co., Ltd. | PVDC | SUMILITE® PVC |
| Surlyn® 1605SBR | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| Elastron® G G100.A55.N | Elastron USA, Inc. | SEBS | Elastron® G |
| LUVOCOM® 80-8222 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Plenco 04466 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |