Lucon® PO6063
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rO6GXC_Lucon-PO6063.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucon® PO-6063 is a Polyphenylene Ether + PS (PPE+PS) material filled with carbon fiber, carbon nano and glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lucon® PO-6063 are:
Typical application of Lucon® PO-6063: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/10.0 kg) | 37 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 98.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 9510 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 142 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 131 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+6 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.00 to 0.981 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® PP HLS-080SP | Saudi Polymers Company | PP Homopolymer | Marlex® PP |
| SureSpec IP-200 | Genesis Polymers | PP Impact Copolymer | SureSpec |
| Fainplast PVC KLT 87/UV | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| HANWHA LDPE 5318 | Hanwha Chemical | LDPE | HANWHA LDPE |
| TOTAL Polyethylene Bio TPSeal® 1100_03 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |