Pinnacle PP 6199C3
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Pinnacle Polymers |
| Trademark: | Pinnacle PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rNwy2v_Pinnacle-PP-6199C3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
100 MELT FLOW CLARIFIED RANDOM COPOLYMER FOR INJECTION MOLDING Pinnacle Polymers Polypropylene 6199C3 is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This product is intended for injection molding applications that require very high melt flow, more stiffness, faster cycle time, low bloom, enhanced processability and excellent clarity. This product contains a new generation clarifier. The 6199C3 product provides:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 100 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, 3.20 mm, Injection Molded) | 14 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(3.20 mm, Injection Molded) | 1100 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C, 3.20 mm, Injection Molded) | 48 | J/m | ASTM D256 |
| Notched Izod Impact (Area) 5(23°C, 3.20 mm, Injection Molded) | 4.70 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Haze (1270 µm) | 10 | % | |
| Yellowness Index | < -10 | YI |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 1.3 mm/min |
| 4 . | Type I |
| 5 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECDUR® B DF 30 SCHWARZ-14345 | LEIS Polytechnik - polymere Werkstoffe GmbH | PBT+ASA | TECDUR® |
| Badamid® LA70 GF50 MoS2 1% | Bada AG | Nylon 66 | Badamid® |
| Fainplast PVC GS 65/C | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Fiberfil® J-60/20/TT/FD WT8381 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Plexar® PX6005 | LyondellBasell Industries | PP, Unspecified | Plexar® |