Eltex® PF6220AE
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rNogSE_Eltex-PF6220AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eltex® PF6220AE has been developed for use in food packaging and other thin film applications where excellent mechanical and optical performance is required. In addition, Eltex® PF6220AE offers easy extrudability. Benefits and Features Eltex® PF6220AE is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
We recommend that you consult your INEOS technical representative for further advice on the use of Eltex® PF6220AE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% Secant, MD : 25 µm | 160 | MPa | |
| 1% Secant, TD : 25 µm | 195 | MPa | |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 25 µm | 9.00 | MPa | |
| TD : Yield, 25 µm | 10.0 | MPa | |
| MD : Break, 25 µm | 60.0 | MPa | |
| TD : Break, 25 µm | 60.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 25 µm | 620 | % | |
| TD : Break, 25 µm | 700 | % | |
| Dart Drop Impact (25 µm) | > 1000 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 220 | g | |
| TD : 25 µm | 450 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 65 | ASTM D2457 | |
| Haze (25.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Conditioning ISO 1872/1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Accura® 55 | 3D Systems | Unspecified | Accura® |
| KOPLA PA66 KDX1083 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Larpeek 50 | LATI S.p.A. | PEEK | Larpeek |
| INEOS PP H03W-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Laprene® 830000547 | SO.F.TER. SPA | SEBS | Laprene® |