HIPTEN® 22003
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rNlAMk_HIPTEN-22003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPTEN® 22003 is low density polyethylene resin developed for production of heavy-duty tubular film. HIPTEN® 22003 has outstanding mechanical properties, good optical properties and very good processability. Extruded films have good toughness, resistance to environmental stress cracking and homogeneous appearance. Production of heavy-duty bags for packaging industrial products ( fertilizers, solid chemicals, pellets etc.), heavy-duty shrink films, etc. HIPTEN® 22003 has Health Certificate issued by Institute for Health Protection of Serbia. Also, has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.0 | MPa | ISO 527-2 |
| Fracture | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 700 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ISO 1184 | ||
| TD : Yield, 40 µm | 11.0 | MPa | ISO 1184 |
| MD : Break, 40 µm | 26.0 | MPa | ISO 1184 |
| TD : Break, 40 µm | 23.0 | MPa | ISO 1184 |
| Tensile Elongation | |||
| MD : Break, 40 µm | 400 | % | ISO 1184 |
| TD : Break, 40 µm | 650 | % | ISO 11925-2 |
| Dart Drop Impact (40 µm) | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 135.1 | kN/m | ASTM D1922 |
| TD : 40.0 µm | 193.0 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 1.6:1 to 3:1 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell RP271G | LyondellBasell Industries | PP Random Copolymer | Purell |
| SLOVAMID® 66 GF 30 FRG 5 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| ARMAMID® PA NE 30-2TAF | Poly Plastic | Nylon 6 | ARMAMID® |
| Loyblend® TA-1030FR | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| TECHNYL® C 236 V35 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |