Romiloy® 3020/01 M10
| Category: | ASA+Nylon , Acrylonitrile Styrene Acrylate + Nylon |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rNkZNA_Romiloy-3020-01-M10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy® 3020/01 M10 is an Acrylonitrile Styrene Acrylate + Nylon (ASA+Nylon) material filled with 10% mineral. It is available in Europe. Important attributes of Romiloy® 3020/01 M10 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 22 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.50 to 0.90 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 52.0 | 37.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 30 | -- | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2400 | 1200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 76.0 | 42.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.5 | -- | kJ/m² | |
| 23°C | 7.5 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | -- |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | -- | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-747S | CHI MEI CORPORATION | ABS | POLYLAC® |
| RTP 205 FR BAC | RTP Company | Nylon 66 | RTP |
| Mold Max® 20 | Smooth-On, Inc | Silicone | Mold Max® |
| TEREZ PA 6.6 7510 GF 30 HY | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Gallonprene® GP420-7007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |