INSTRUC PPAGF30

Category:	PPA , Polyphthalamide
Manufacturer:	Infinity LTL Engineered Compounds
Trademark:	INSTRUC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rNGE2e_INSTRUC-PPAGF30.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Instruc glass and carbon fiber reinforced, mineral and process additive filled structural compounds - Offered in all Infinity base resins

Provide significant improvements in strength, stiffness, creep resistance, fatigue endurance and impact & dimensional stability

Increased thermal HDTUL and long term heat resistance

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	Fatigue Resistant Good Creep Resistance Good Dimensional Stability Good Heat Aging Resistance Good Impact Resistance High Flow High Stiffness High Strength Medium Heat Resistance
Uses	Structural Parts

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.44	g/cm³	ASTM D792
Specific Volume	0.694	cm³/g
Molding Shrinkage - Flow	0.20 to 0.30	%	ASTM D955
Water Absorption (24 hr)	0.20	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	125		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	207	MPa	ASTM D638
Tensile Elongation (Yield)	1.0 to 3.0	%	ASTM D638
Flexural Modulus	11000	MPa	ASTM D790
Flexural Strength	276	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	80	J/m	ASTM D256
Unnotched Izod Impact (3.18 mm)	640	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	282	°C	ASTM D648
CLTE - Flow	2.3E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+17	ohms	ASTM D257

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.59 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	135	°C
Drying Time	4.0	hr
Processing (Melt) Temp	329	°C
Mold Temperature	135	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	40 to 70	rpm
Vent Depth	0.013 to 0.025	mm

Resin Grade	Manufacturer	Category	Trademark
Matrixx 15S3302	The Matrixx Group, Inc.	PP, Unspecified	Matrixx
RTP 983	RTP Company	PSU	RTP
Tenite™ Butyrate 550E4861316 Clear, Trsp	Eastman Chemical Company	CAB	Tenite™ Butyrate
Witcom PP H/4L1-HS	Witcom Engineering Plastics B.V.	PP Homopolymer	Witcom PP
Hyundai EP PA66 LD460Z	HYUNDAI EP Co., Ltd.	Nylon 66	Hyundai EP PA66