Clear-Flex® 95
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Clear-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rMUgKn_Clear-Flex-95.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clear Flex®50 and Clear Flex® 95 are water white clear urethane liquid rubber compounds designed for applications that require absolute clarity and resistance to sunlight. Low viscosity ensures easy mixing and pouring. Clear Flex® 50 and 95 cure at room temperature with negligible shrinkage. Cured castings are clear, flexible and UV Resistant. Vibrant colors and color effects are achieved by adding pigments. Applications include making clear-cut molds, model reproductions, decorative cast pieces, special effects, prototype parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.968 | cm³/g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time | 16.0 | hr |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.28 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 23°C) | 95 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 17.2 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 180 | % | ASTM D412 |
| Tear Strength 1(23°C) | 35.0 | kN/m | ASTM D624 |
| Optical | Nominal Value | ||
|---|---|---|---|
| Refractive Index | |||
| -- 2 | 1.492 | ||
| -- 3 | 1.493 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.5 | ||
| Pot Life | 25 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 250 | cP | ASTM D2393 |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | 25°C |
| 3 . | 20°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9714-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® CP-13066 NAT XRD1 | Teknor Apex Company | TPE | Monprene® |
| Daelim Po1y® PP-137T | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Hanwha Total PP TB92R | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| 3M™ Dyneon™ PTFE Compound TF 6419 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |