Witcom PA6 2004/39
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rLMMlG_Witcom-PA6-2004-39.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PA6 2004/39 is a polyamide 6 (nylon 6) product that contains a filler. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 - 0.40 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 6.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -40°C | 7600 | MPa | ISO 527-2 |
| 23°C | 7000 | MPa | ISO 527-2 |
| 80°C | 3600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, -40°C | 155 | MPa | ISO 527-2 |
| Fracture, 23°C | 110 | MPa | ISO 527-2 |
| Fracture, 80°C | 65.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Fracture, -40°C | 1.0 - 3.0 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 4.0 | % | ISO 527-2 |
| Fracture, 80°C | 5.0 - 7.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 50 | kJ/m² | ISO 180/1U |
| 23°C | 60 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| CLTE - Flow | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 95.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 83MF10 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Cariflex® IR0307 K | Kraton Polymers LLC | IR | Cariflex® |
| Flontech® FT-PI15-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Generic PUR-Eth,aliphat | Generic | PUR-Eth,aliphat | Generic |
| SURPASS® HPs019-F | NOVA Chemicals | LLDPE | SURPASS® |