MonoSol® E6030C
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rLARCh_MonoSol-E6030C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol E6030C is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol's proprietary solution cast technology. MonoSol E6030C is an embossed rapidly dissolving clear PVOH film used for unit dose packaging of industrial and household cleaning compounds. Its relatively high modulus makes it particularly suitable for small pouching and tight wrapping applications. This film is commonly used for Toilet Block Disinfectants, Deodorizers and Cleaners and is converted on conventional pleat wrapping and flow-wrapping. Standard thicknesses are 20 micron (0.8 mil) and 25 micron (1.0 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 5.2 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 25.4 µm | 6.0 | sec | |
| Disintegration : 24°C, 25.4 µm | 3.0 | sec | |
| Dissolution : 10°C, 25.4 µm | 22.0 | sec | |
| Dissolution : 24°C, 25.4 µm | 15.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (25.4 µm) | 2.99 | m²/kg | ASTM D4321 |
| Film Thickness - Recommended / Available | 20 µm and 25 µm | ||
| Secant Modulus - 100%, MD | 21.7 | MPa | ASTM D882, ISO 527-3 |
| Tensile Strength - MD | |||
| Break | 25.2 | MPa | ASTM D882 |
| -- | 25.2 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Break) | 280 | % | ASTM D882, ISO 527-3 |
| Dart Drop Impact (25 µm) | 300 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength - MD | |||
| -- | 830 | g | ASTM D1922 |
| -- | 0.084 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66GF43HRN | A. Schulman Inc. | Nylon 66 | SCHULAMID® |
| K-Bin Rigid PVC KBD-5001 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| LG ABS LG749W | LG Chem Ltd. | ABS | LG ABS |
| LNP™ THERMOCOMP™ Lexan_LGK3020 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| RTP 899 X 141392 C NS | RTP Company | Acetal (POM) Copolymer | RTP |