Innothane® IE-3031
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rKfeQd_Innothane-IE-3031.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-3031 is a rigid polyurethane formulated for room temperature hand-batch or meter-mix equipment. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. It has excellent green strength yielding enhanced demold characteristics and also yields easy to paint surfaces requiring little preparation. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.08 | g/cm³ | |
| Hardener | 1.08 | g/cm³ | |
| Base Resin | 1.19 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 75.0 | °C | |
| 1.8 MPa, Unannealed | 70.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 91 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 7.5 to 13 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.075 | Pa·s | |
| 25°C 2 | 0.15 | Pa·s | |
| 25°C 3 | 0.45 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 1.5 to 2.5 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 80 | ASTM D2240 | |
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation at Break | 20 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3H | RTP Company | Nylon 66 | RTP |
| Fainplast PVC KL 96/5 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| PENTAMID B GV10 MC20 H RC schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| RTP 199 X 141356 | RTP Company | PP, Unspecified | RTP |
| Osterlene® HD0954 | Osterman & Company | HDPE | Osterlene® |