Moplen RP348R
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rKc96K_Moplen-RP348R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen RP348R is a nucleated and antistatic additivated random copolymer for injection moulding that displays excellent transparency combined with good flowability. The main applications of Moplen RP348R are housewares and caps & closures. For regulatory information please refer to Moplen RP348R Product Stewardship Bulletin ( PSB ) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| -- | 25 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 25 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 60.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 29.0 | MPa | ASTM D638 |
| Yield | 30.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 13 | % | ASTM D638 |
| Yield | 14 | % | ISO 527-2 |
| Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1050 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 3.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 76.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 72.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 85 | ASTM D2457 | |
| Haze (1000 µm) | 9.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tygon SE-200 | Saint Gobain - Norton | PVC, Unspecified | Tygon |
| Chemlon® 120 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| LUVOCOM® 1850-7581 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| MAJORIS DW374 - 8229 | AD majoris | PP Copolymer | MAJORIS |
| SQUARE® SR8656A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |