SUMIPLOY® FS2200
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIPLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rI1Tc3_SUMIPLOY-FS2200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUMIPLOY® FS2200 is a Polyethersulfone (PESU) material. It is available in Asia Pacific or North America for injection molding. Important attributes of SUMIPLOY® FS2200 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption (24 hr) | 0.39 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 77.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 78 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | 980 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 203 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -50 to 150°C | 5.9E-5 | cm/cm/°C | |
| Transverse : 50 to 150°C | 6.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Arc Resistance | 80.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.430 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 340 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 351FA | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Nypol® PA A3 T40 PRTA011 NR321 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Nypol® PA A3 HF NTLA010 NR430 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Cheng Yu FV30G15 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Karina CLEAR PVC COMPOUND 90/210 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |