ENGAGE™ 8401
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rHo62K_ENGAGE-8401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8401 Polyolefin Elastomer is an ethylene-octene copolymer that offers excellent performance in durable, flexible injection molded industrial and consumer goods. ENGAGE 8401 provides high clarity in products requiring visual inspection and allows the use of hot runner molds to enhance production efficiency. In addition, its low density can help control resin and production costs, while reducing the weight of end products. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.885 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 2 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 84 | ||
| Shore D, 1 sec, Compression Molded | 26 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 4.00 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 8.50 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 940 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 30.7 | MPa | |
| 2% Secant : Compression Molded | 30.6 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 56.2 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -47.0 | °C | Internal Method |
| Vicat Softening Temperature | 49.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 80.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 59.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Metabolix I6003rp | Metabolix | PHA | Metabolix |
| Veroplas 400T | PlastxWorld Inc. | ABS | Veroplas |
| Andur 5 DPLM | Anderson Development Company | PUR-Ester/TDI | Andur |
| Karina IVORY PVC COMPOUND 803-35/1-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Moplen HP500N | LyondellBasell Industries | PP Homopolymer | Moplen |