| Category: | PESU , Polyethersulfone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latishield |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rGN7WE_Latishield-85-08A-G-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMI shielding product based on Polyethersulphone (PES). UL94 V-0 classified, halogens free. Steel fibres. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 0.90 | % | |
| Flow : 2.00 mm | 0.35 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| Ball Pressure Test | > 165 | °C | IEC 60335-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electromagnetic Reflection | 90 | % | |
| Surface Resistivity | 8.0 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 300 to 340 | °C | |
| Mold Temperature | 100 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 101 Z | RTP Company | PP, Unspecified | RTP |
| SMOKEGUARD™ III 1080-C NATURAL | AlphaGary | PVC, Unspecified | SMOKEGUARD™ III |
| CP PRYME® Polycarbonate PC100RULUV-10M BT Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| LUVOCOM® 20-7847 VP | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| Durethan® BKV 25 FN27 000000 | LANXESS GmbH | Nylon 6 | Durethan® |