LONGLITE® PBT 7030-200X
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rGGZG9_LONGLITE-PBT-7030-200X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/ASA 7030-200X is a 30% glass fiber reinforced natural color injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 1.1 | % | |
| Flow | 0.10 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 160 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C) | 230 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen Q30G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Vyncolit® E 2748-9641CB | Vyncolit N.V. | Epoxy | Vyncolit® |
| Geon™ Vinyl Rigid Extrusion 87567 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hostacom EPKC10ZC | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 4200-88UV White 1523 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |