PLANAC BT-1000-S01
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PLANAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rGD1eU_PLANAC-BT-1000-S01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PLANAC BT-1000-S01 is a polybutene terephthalate (PBT) product,. It can be processed by injection molding and is available in North America or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.9 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638 |
| Tensile Strength | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Compressive Strength | 85.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 42 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 160 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value shown for Comparative Track Index, UL 746, was tested in accordance with ASTM D3638.Flexural Elongation @ Break, ASTM D790: NB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Mold Temperature | 20.0 - 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Impact 945E | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| FRIANYL® A3 GF07 V2XI | Nilit Plastics | Nylon 66 | FRIANYL® |
| Laticonther 80 CPG/700 | LATI S.p.A. | PPS | Laticonther |
| Plaslube® PA6/6 CF30 TS12 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Teldene® H08CFM | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |