Amilan® CM3511G50
| Category: | Nylon Copolymer , Polyamide Copolymer |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rFrVsT_Amilan-CM3511G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM3511G50 is a Polyamide Copolymer (Nylon Copolymer) product filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.50 to 0.70 | % | |
| Flow : 3.00 mm 2 | 0.20 to 0.40 | % | |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 210 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.2 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 14500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 320 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 28 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 215 | °C | ISO 75-2/B |
| Melting Temperature | 216 | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1500 | J/kg/°C | |
| Thermal Conductivity | 0.40 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech P240 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| XANTAR® 18 SR FD | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| NOVALAC RX®525 | Vyncolit N.V. | Phenolic | NOVALAC |
| KOPEL® KP3335 | Kolon Plastics, Inc. | TPC-ET | KOPEL® |
| LUVOTECH® MR 2007/BL | LEHVOSS Group | Nylon 6 | LUVOTECH® |