PRL PC-GP2-D
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rDqBRN_PRL-PC-GP2-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC-GP2-D is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 to 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 70 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 62.1 | MPa | |
| Break, 3.18 mm | 68.9 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 6.5 | % | |
| Break, 3.18 mm | 140 | % | |
| Flexural Modulus (3.18 mm) | 2310 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 95.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 800 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | > 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 135 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 129 | °C | |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 1 |
| RTI Elec | UL 746 | ||
| 0.750 mm | 80.0 | °C | |
| 1.50 mm | 125 | °C | |
| 3.00 mm | 125 | °C | |
| RTI Imp | UL 746 | ||
| 0.750 mm | 80.0 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C | |
| RTI Str | UL 746 | ||
| 0.750 mm | 80.0 | °C | |
| 1.50 mm | 125 | °C | |
| 3.00 mm | 125 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.750 mm) | 28 | kV/mm | ASTM D149 |
| Arc Resistance (0.750 mm) | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) (0.750 mm) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 1 | ||
| High Voltage Arc Tracking Rate (HVTR) (0.750 mm) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 2 | ||
| 3.00 mm | PLC 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, ALL | V-2 | ||
| 1.50 mm, ALL | V-2 | ||
| 3.00 mm, ALL | V-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 to 124 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1173A | Teknor Apex Company | TPE | Telcar® |
| Topilene® J440F | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Tuftec™ M1943 | AKelastomers | SEBS | Tuftec™ |
| TRIMID® N66-G33HL | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Hax™ HF 039/4H | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |