Rigid Cast RC-8006 FR
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | Rigid Cast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rDlqhA_Rigid-Cast-RC-8006-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rigid-Cast 8006 FR A/B produces a tough, rigid 78 Shore D urethane based material for use in making small detailed parts, models, prototypes and limited runs of production parts. This material has a convenient 1 to 2 parts by volume ratio, with an approximate three-minute working time, ideal for hand dispensing using dual cartridge static mix equipment. Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Shrinkage | |||
| 6.35 mm 1 | 0.30 | % | |
| 6.35 mm 2 | 0.20 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Time (25°C) | 2.5 to 3.0 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 76 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 896 | MPa | ASTM D638 |
| Tensile Strength | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.8 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 64.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 26 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 87.8 to 93.3 | °C | |
| 1.8 MPa, Unannealed | 82.2 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 50, Mix Ratio by Volume: 50 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity | 800 | cP | ASTM D2393 |
| Demold Time | 45 to 60 | min | |
| Post Cure Time (25°C) | 2.0 to 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | Post-cure, Method 1 |
| 2 . | 7-day ambient cure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vibrathane® 6060 | Chemtura | PUR-Capro/TDI | Vibrathane® |
| CALP E4331 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| APEX® 3302-70NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Huaxia Shenzhou DS608-C | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluoropolymer | Huaxia Shenzhou |
| Sylvin 2910-45 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |