TAROPRENE® 1 A70 E1N
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROPRENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rC7llg_TAROPRENE-1-A70-E1N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Elastomer Vulcanized. This TPE-V compound combines the typical performance of a vulcanized elastomer with the easy processing of a thermoplastic compound. Taroprene is totally recyclable and it can be produced in standard grades and in tailor-made grades. Available in natural, black and colored grade. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 70 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain | 3.00 | MPa | |
| 300% Strain | 5.10 | MPa | |
| Tensile Strength 2(Break) | 6.80 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 480 | % | ASTM D412 |
| Tear Strength | 25.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 70°C, 22 hr | 35 | % | |
| 100°C, 22 hr | 40 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 170 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | Die C |
| 3 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201.3A HS | RTP Company | Nylon 6 | RTP |
| Bayblend® FR3000 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| DuraGrip® DGR 6230TR | Advanced Polymer Alloys | TPE | DuraGrip® |
| Hostaform® C 9021 M | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Polifil® PP C-10 | The Plastics Group | PP Homopolymer | Polifil® PP |