Ducor® 1087 K
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | Ducor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rByuD8_Ducor-1087-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ducor 1087K is a polypropylene homopolymer for extrusion- & thermoforming applications, requiring high transparency and improved stiffness. The product is nucleated and clarified, and contains antistatic agents. Ducor 1087K exhibits excellent processability, and very good optical and mechanical properties of thermoformed parts. Food Contact Applications: This grade is in compliance with most regulations regarding food contact applications (EU, FDA). Specific information is available upon request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.1 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 79.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1850 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 37.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 7.0 | % | |
| Break | > 25 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 150 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ISO 306/A |
| -- | 94.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm, Injection Molded) | 30 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Celstran® +PP-GF60-04CN15 | Celanese Corporation | PP, Unspecified | Celstran® |
| DESLON™ 6 DSC121A | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| Eltex® A3180N1852 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| LIHAN® B705 | Nanjing Lihan Chemical Co., Ltd. | Nylon 6 | LIHAN® |
| ESTOPLAST ZK 6002NN05 | Ester Industries Ltd. | PC | ESTOPLAST ZK |