Radel® R-7535
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Radel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rBo38E_Radel-R-7535.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Radel® R-7535 polyphenylsulfone resin is a cost-effective solution for aircraft interior applications. This product complies with the FAA regulation 14CFR Part 25 Appendix F, offering vertical burn resistance, very low smoke generation and, through the use of proprietary additives, low heat release values by the Ohio State University (OSU) rate of heat release method. It also generates low flaming-mode toxic gas emissions. Radel® R-7535 is formulated for darker, integrally colored applications where there is low UV exposure. An alternate grade, Radel® R-7558, is available for lighter applications with low UV exposure.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.36 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 196 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| OSU Peak Heat Release Rate 1 | < 55.0 | kW/m² | FAR 25, AppF |
| OSU Total Heat Release - 2 min 2 | < 20.0 | kW·min/m² | FAR 25, AppF |
| Smoke Density - Dmax @ 4 min 3 | < 5.0 | Ds | FAR 25, AppF |
| Vertical Burn - 60 second 4 | FAR 25, AppF | ||
| Drip Burn Time | No Drip | ||
| Flame Time | 0.0 | hr | |
| Length | < 7.62 | cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 166 to 177 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 354 to 371 | °C | |
| Middle Temperature | 360 to 377 | °C | |
| Front Temperature | 366 to 382 | °C | |
| Nozzle Temperature | 360 to 377 | °C | |
| Processing (Melt) Temp | 366 to 388 | °C | |
| Mold Temperature | 107 to 163 | °C | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Flammability test results are not intended to reflect hazards presented by these or any other material under actual fire conditions. |
| 2 . | Flammability test results are not intended to reflect hazards presented by these or any other material under actual fire conditions. |
| 3 . | Flammability test results are not intended to reflect hazards presented by these or any other material under actual fire conditions. |
| 4 . | Flammability test results are not intended to reflect hazards presented by these or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 GF 10 GB 20 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| TOTAL Polyethylene LDPE LA 0710 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Tuftec™ H1031 | AKelastomers | SEBS | Tuftec™ |
| Sylvin 83007-67 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Infino SA-1100 | LOTTE ADVANCED MATERIALS CO., LTD. | PC | Infino |