ACCUTECH™ CP0437M40CL
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rB1xTW_ACCUTECH-CP0437M40CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™CP0437M40CL is a polypropylene copolymer (PP Copoly) product, which contains 40% mica filler. It is available in North America. The main characteristics are: chemical coupling. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 36 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 19.0 | MPa | ASTM D638 |
| Fracture | 18.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.0 | % | ASTM D638 |
| Fracture | 3.0 | % | ASTM D638 |
| Flexural Modulus | 3800 | MPa | ASTM D790 |
| Flexural Strength | 26.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 117 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® HTN FE350038 BK083 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Boda BDBR-H5801 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| ARC ARC6604 | ARC Resin Corporation | Nylon 66 | ARC |
| HiFill® PA6/6 GF15 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| LNP™ STAT-KON™ RD000I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |