XENOY™ X5630Q resin
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r9yYPi_XENOY-X5630Q-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.42 | % | |
| Equilibrium, 23°C, 50% RH | 0.14 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4150 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 56.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.2 | % | |
| Break | 8.0 | % | |
| Flexural Modulus 2 | 4050 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 110 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ISO 306/B50 |
| -- | 140 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 80°C | 5.2E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 7.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 250 to 275 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 265 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOLEN R030 BM | SIBUR, LLC | PP Random Copolymer | TOLEN |
| Westlake PVC 1230P | Westlake Chemical Corporation | PVC, Rigid | Westlake PVC |
| Fiberfil® PP-62/CC/20/UV | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| ESENTTIA 18H86 | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Polifil® PS RP-HIPS | The Plastics Group | PS (HIPS) | Polifil® PS |