Nypol® PA A3 G30 HS UV RH NTLA013 NR414
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r8vwnR_Nypol-PA-A3-G30-HS-UV-RH-NTLA013-NR414.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 slightly greenish natural reinforced with 30% of fiberglass, heat stabilized, resistance to hydrolysis and UV. Good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 to 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 1.5 | -- | % | ISO 62 |
| Relative Viscosity 1 | 46.0 to 52.0 | -- |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 230 | 150 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 200 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.2 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 12200 | 6500 | MPa | ISO 178 |
| Flexural Stress | 290 | 210 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | -- | 70 | kJ/m² | |
| 23°C | 12 | 16 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | -- | 70 | kJ/m² | |
| 23°C | 11 | 14 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 250 to 265 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 270 to 285 | °C | |
| Mold Temperature | 100 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Formic Acid |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zythane® 7070A | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| Jam LL-32604/UV | Jam Petrochemical Company | LLDPE | Jam |
| Delene 2030 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |
| Sylvin 8865-75FUV Yellow 4162 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ UF006S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |